• Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode
  • Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode
  • Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode
  • Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode
  • Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode
  • Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode

Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode

Type: H (Heat Resistant Low Alloy Steel/ Stainless Steel Electrode)
Material: Stainless Steel
Diameter: 2.0/2.5/3.2/4.0/5.0mm
Length: 300-400mm
Welding Core Type: Stainless Steel
Electrode Coating Type: Rutile
Samples:
US$ 30/kg 1 kg(Min.Order)
| Request Sample
Customization:
Gold Member Since 2022

Suppliers with verified business licenses

Manufacturer/Factory

Basic Info.

Model NO.
E308L-16
Slag Characteristic
Acidic
Stainless Steel Welding Rod Type
Chromium Stainless Steel
Function
Surfacing Electrode
Welding Power
AC/DC
Transport Package
Carton + Wooden Pallet
Specification
20KG/box
Origin
Chenzhou Hunan China
HS Code
8311100000
Production Capacity
100000ton/Year

Product Description

E308L-16 is a Rutile type coated electrode. Both alternative current(AC) and direct current (DC) can be applied. It can be welded in all positions. The welding performance is excellent. The arc is stable. The welding spatter is small and the welding slag is easy to remove. The welding bead appearance is beautiful. Welding Deposits exhibits good corrosion-resistance. E308-16 is widely used on common stainless steel welding and Corrosion-resistant stainless steel structure with temperature below 300 degrees Celsius.  Before use, it must be baked at 320-350 degrees Celsius for 1 hour. It can be used anytime after bake. The welding current should not be too high and the amplitude should not be too large.
Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode Welding Rod A002 Stainless Steel Electrode E308L-16 2.5/3.2/4.0mm Manufacturer OEM Rutile Coated Pressure Welding Electrode

Send your message to this supplier

*From:
*To:
avatar Mr. he
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Gold Member Since 2022

Suppliers with verified business licenses

Manufacturer/Factory
Number of Employees
87
Year of Establishment
2010-10-09